The reason of tungsten carbide mold parts abrasion
article source:  Executive editor:Catherine  View:2477  Publish time:2014-12-31

Many friends who are in the mold industry have some knowledge about tungsten carbide mold parts. But in the process of tungsten carbide mold parts production and processing, they will all in wear and tear. What caused the tungsten carbide mold parts abrasion? I believe that many friends are not very understand it. Next, I will analyze the reason of tungsten carbide mold parts abrasion for you.
A.Oxidative wear
After the operation temperature of tungsten carbide mold parts is over 700 ℃, the oxygen in the air will react with chemicals in the tungsten steel. Then, it will form the loose and vulnerable oxide on the surface. When the oxide are wiped off by mechanical action, tungsten carbide mold parts will be corroded and abraded and left pits on the surface.
B. Mechanical abrasion and wear
The workpiece material, Such as the metal carbides, rub and scratch on the surface of tungsten carbide mold parts. Due to the mechanical action, it gradually erase the surface material and then cause the wear and tear. Mechanical abrasion and wear exists under any cutting speed.
C. Diffusive wear 
The higher the cutting temperature, the faster the diffusion, and the more quickly the tungsten carbide mold parts abrasion. It is closely related to the properties of tungsten carbide mold parts.
D. Bond wear
 Under the condition of high cutting temperature, some outstanding points of tungsten carbide mold parts will bond with the workpiece, and gradually be cut, teared and taken away by the workpiece. This is bond wear.